固溶强化型镍基合金的时效析出行为

doi:10.11930/j.issn.1004-9649.2013.9.34.4

中国电力 ›› 2013, Vol. 46 ›› Issue (9): 34-38.DOI: 10.11930/j.issn.1004-9649.2013.9.34.4

固溶强化型镍基合金的时效析出行为

郭岩^{1, 2}, 侯淑芳², 王博涵², 林琳²

1. 西安交通大学材料科学与工程学院,陕西西安 710048; 2. 西安热工研究院有限公司,陕西西安 710032

收稿日期:2013-04-25 出版日期:2013-09-23 发布日期:2015-12-10
作者简介:郭岩（1977—）,男,福建福安人,高级工程师,博士,从事超超临界火电机组材料研究。
基金资助:
2010年度中国电机工程学会电力青年科技创新资助项目

Aging Precipitation Behavior of Solid-Solution Strengthened Nickel-Base Alloys

GUO Yan^{1, 2}, HOU Shu-fang², WANG Bo-han², LIN Lin²

1. School of Materials Science and Engineering, Xi’an Jiaotong University, Xi’an 710048, China; 2. Xi’an Thermal Power Research Institute Co. Ltd., Xi’an 710032, China

Received:2013-04-25 Online:2013-09-23 Published:2015-12-10

摘要/Abstract

摘要： 为了给700 ℃超超临界机组选材提供技术参考,研究了2种固溶强化型镍基合金（617和625）经时效处理（时效）后的析出行为。结果表明：2种镍基合金760 ℃时效后,均析出M₂₃C₆、M₆C碳化物和γ′相;M₂₃C₆、M₆C碳化物分布于晶界和晶内,γ′相分布于晶内;γ″相在625合金晶界、层错处析出并向晶内生长。617合金时效3 000 h,晶界析出相不连续分布;时效5 000 h后晶界析出相聚集且连续分布,晶内析出相的尺寸基本稳定。625合金时效3 000 h的晶内析出相尺寸无明显变化,晶界M₂₃C₆颗粒聚集长大;时效5 000 h后M₂₃C₆转变为M₆C碳化物。617合金和625合金时效后的冲击吸收能量均明显下降,时效后的625合金脆化程度较时效后的617合金严重。

关键词: 超超临界机组, 选材, 617合金, 625合金, 时效处理, 析出相, 脆化

Abstract: Aging precipitation behavior of the two solid-solution strengthened Ni-based alloys(617 and 625) has been investigated. The results revealed that the M₂₃C₆ and M₆C carbide particles precipitated both at the grain boundaries and inside grains, and the γ phase particles were situated at intragranular sites in the process of aging at 760 ℃ for two alloys. In addition, γ″ phase precipitated at grain boundaries and stacking faults in the aged alloy 625. The carbide particles discontinuously dispersed at grain boundaries after aging for up to 3 000 h for alloy 617; however, the 5 000 h aging induced the coalescence of the carbide particles. After aging up to 5 000 h, the size of precipitates inside grains remained basically stable for alloy 617. The carbides precipitates dispersed continuously at inter-granular site were observed in the alloy 625 aged for 3 000 h and an increase of aging time resulted in the growth of carbide particles. The size of intragranular particles kept almost unchanged after aging for up to 3 000 h for alloy 625; however, the presence of a number of M₆C particles was visible for alloy 625 after 5 000 h. The impact absorbed energy obviously declined for two alloys after aging. Aging embrittlement of the alloy 625 is greater than that of the alloy 617.

Key words: USC unit, material selection, alloy 617, alloy 625, aging, precipitation, embrittlement

中图分类号:

TK225

郭岩, 侯淑芳, 王博涵, 林琳. 固溶强化型镍基合金的时效析出行为[J]. 中国电力, 2013, 46(9): 34-38.

GUO Yan, HOU Shu-fang, WANG Bo-han, LIN Lin. Aging Precipitation Behavior of Solid-Solution Strengthened Nickel-Base Alloys[J]. Electric Power, 2013, 46(9): 34-38.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.electricpower.com.cn/CN/10.11930/j.issn.1004-9649.2013.9.34.4

https://www.electricpower.com.cn/CN/Y2013/V46/I9/34

参考文献

[1] 赵双群,谢锡善. 一种新型镍基高温合金长期时效后的组织和性能[J]. 金属学报,2003,39（4）：399-404.
ZHAO Shuang-qun, XIE Xi-shan. Properties and microstructure after long term aging at different temperatures for a new nickel base superallo [J]. Acta Metallurgica Sinica, 2003, 39(4): 399-404.
[2] 胡正飞,吴细毛,张斌,等. 长期服役的12%Cr马氏体耐热钢中的碳化物及其变化[J]. 动力工程学报,2010,30（4）：269-274.
HU Zheng-fei, WU Xi-mao, ZHANG Bin, et al . The evolution of carbides in 12%Cr heat-resistant steel for long-term service at elevated temperature[J]. Journal of Chinese Society of Power Engineering, 2010, 30(4): 269-274.
[3] 郭岩,林琳,侯淑芳,等. 国产TP310HCbN钢在高温应力下的组织结构[J]. 中国电力,2012,45（10）：42-47.
GUO Yan, LIN Lin, HOU Shu-fang, et al . Microstructure of domestic TP310HCbN steel after high-temperature creep-rupture test [J]. Electric Power, 2012, 45(10): 42-47.
[4] CABIBBO M, GARIBOLDI E, SPIGARELLI S, et al . Creep behavior of incoloy alloy 617[J]. Journal of Materials Science,2008, 43(8): 2912-2921.
[5] RAHMAN S, PRIYADARSHAN G, RAJA K S, et al . Investigation of the secondary phases of alloy 617 by scanning kelvin probe force microscope [J]. Materials Letters, 2008, 62(15): 2263-2266.
[6] GARIBOLDI E, CABIBBO M, SPIGARELLI S. Investigation on precipitation phenomena of Ni-22Cr-12Co-9Mo alloyaged and crept at high temperature[J]. International Journal of Pressure Vessels and Piping, 2008, 85(1/2): 63-71.
[7] MATHEW M D, PARAMESWARAN P, BHANU SANKARA RAO K. Microstructural changes in alloy 625 during high temperature creep[J]. Materials Characterization, 2008, 59(5):508-513.
[8] TAWANCY H M, ALLAM I M, ABBAS N M. Effect of Ni3Nb precipitation on the corrosion resistance of inconel alloy 625[J]. Journal of Materials Science Letter, 1990, 9(3): 343-347.
[9] SHAIKH M A, AHMAD M, SHOAIB K A. Precipitation hardening in Inconel 625 [J]. Materials Science and Technology, 2000, 16(2): 129-132.
[10] 李玉清,刘锦岩. 高温合金晶界间隙相[M]. 北京：冶金工业出版社,1990：308-311.
[11] MANKINS W L, HOSIER J C, BASSFORD T H. Microstructure and phase stability ofinconel alloy 617[J]. Metallurgical Transactions, 1974, 5(12): 579-2590.
[12] 奚淑琴. 长期使用及时效后RA333中碳化物的变化[J]. 冶金物理测试,1985（6）：13-16.
XI Shu-qin. The changes of the carbides in RA333 alloy for long-term service at elevated temperature [J]. Physics Examination and Testing, 1985(6):13-16 .
[13] 胡正飞,杨振国. 长期高温时效F12耐热合金钢中碳化物形态和组分变化[J]. 金属学报,2003,39（2）：131-135.
WU Zheng-fei, YANG Zhen-guo. The morphological and compositional changes of the carbides in F12 heaat-resistant alloy steel for long-term service at elevated temperature[J]. Acta Metallurgica Sinica, 2003, 39(2): 131-135.
[14] 崔彤,王磊,杨洪才,等. 长期时效对一种镍基合金组织及冲击性能的影响[J]. 有色矿冶,2005,21（1）：33-36.
CUI Tong, WANG Lei, YANG Hong-cai, et al . Microstructure and impact toughness of a Ni-based superalloy after long-term aging [J]. Non-Ferrous Mining and Metallurgy, 2005, 21(1): 33-36.

[1]	王渡, 刘玉贤, 万明元, 赵思维, 江剑明. 660 MW超超临界机组循环水泵配置及运行方式优化[J]. 中国电力, 2020, 53(2): 112-119.
[2]	张金营, 孙蓟光. 基于控制受限MIMO预测控制的超超临界机组集中式协调控制[J]. 中国电力, 2019, 52(5): 21-28.
[3]	王亚欧, 陶谦, 肖杰, 陈波. 1 000 MW双切圆燃烧锅炉干湿态转换过程中水冷壁温度控制[J]. 中国电力, 2019, 52(1): 161-165,173.
[4]	俞葆青, 彭杏娜, 丛相州, 彭先宽, 杜占江, 高志. 超超临界机组疏水罐罐体泄漏原因分析及防治[J]. 中国电力, 2018, 51(9): 83-87,150.
[5]	孟海洋. 新型国产1 050 MW超超临界机组高压主汽阀卡涩原因分析及改进[J]. 中国电力, 2018, 51(7): 90-94.
[6]	萧嘉繁, 谭厚章, 刘鹤欣, 王毅斌, 董琨. 某1 000 MW超超临界燃煤机组尾部烟道硫酸铵盐沉积分析[J]. 中国电力, 2018, 51(4): 67-74.
[7]	牛海明, 邱忠昌, 黄焕袍. 1 000 MW二次再热超超临界机组再热汽温控制策略及工程应用[J]. 中国电力, 2017, 50(9): 138-142.
[8]	樊印龙, 张宝, 李蔚, 丁阳俊, 顾正皓. 上汽超超临界汽轮机汽门快关控制逻辑优化[J]. 中国电力, 2017, 50(9): 143-147.
[9]	王林, 刘辉, 刘超, 高景辉, 赵志丹, 王红雨, 孟颖琪. 二次再热机组锅炉三段吹管技术研究[J]. 中国电力, 2017, 50(7): 69-73.
[10]	高嵩, 赵洁, 黄迪南. 1 000 MW超超临界二次再热燃煤发电技术[J]. 中国电力, 2017, 50(6): 6-11.
[11]	阳光, 陈仁杰, 朱佳琪. 1 000 MW超超临界二次再热燃煤发电示范工程总体设计方案[J]. 中国电力, 2017, 50(6): 12-16.
[12]	韩宾, 徐庆磊, 胡方, 竺凌, 赵敏凯. 1 000 MW二次再热机组高压加热器系统开发及应用[J]. 中国电力, 2017, 50(6): 17-20.
[13]	黄焕袍, 阳光, 崔青汝. 1 000 MW二次再热超超临界机组分散控制系统关键技术研究及应用[J]. 中国电力, 2017, 50(6): 21-26.
[14]	崔青汝, 牛海明. 1 000 MW二次再热火电机组主蒸汽温度控制策略及工程应用[J]. 中国电力, 2017, 50(6): 27-31.
[15]	张世山, 陈振宇, 郑鹏, 陈鸥, 杨建辉. 国电泰州电厂2×1 000 MW二次再热机组NOx、SO₂超低排放技术应用[J]. 中国电力, 2017, 50(6): 32-37.

固溶强化型镍基合金的时效析出行为

Aging Precipitation Behavior of Solid-Solution Strengthened Nickel-Base Alloys

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

模态框（Modal）标题

固溶强化型镍基合金的时效析出行为

Aging Precipitation Behavior of Solid-Solution Strengthened Nickel-Base Alloys

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics